Aluminum alloy 6082
Produce 1000~8000 All Aluminum Billet
Popular one :Grade 6082
Composition：Si: 0.7～1.3,Fe:<0.5,
Cu<0.1,Mn:0.40～1.0,Mg：0.6～1.2
Cr<0.25,Zn<0.2,Ti<0.1,impurity<0.15
Material for window frame factories.
Parameter
Aluminum bar 6082 Composition | ||||||||||
Grade |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
impurity |
Al |
6082 |
0.7～1.3 |
<0.5 |
<0.1 |
0.40～1.0 |
0.6～1.2 |
<0.25 |
<0.2 |
<0.1 |
<0.15 |
remainder |
More About Aluminum Bar 6082
6082 is a heat-treated Du strengthening alloy with good formability, weldability, machinability and medium strength. It can maintain good operability after annealing. It is mainly used in mechanical structure, including bar, plate, pipe and profile. This alloy has similar but not identical mechanical properties to 6061 alloy, Its - T6 state has high mechanical properties. Alloy 6082 is a very common alloy product in Europe and also has high application in the United States. It is suitable for processing raw materials, seamless aluminum tubes, structural profiles and custom profiles. 6082 alloy usually has good processing characteristics and good anodic reaction performance. The most commonly used anode reaction methods include impurity removal, impurity removal and dyeing, 6082 combines excellent solderability, brazing, corrosion resistance, formability and machinability. The - 0 and T4 states of alloy 6082 are suitable for bending and forming, and - T5 and - T6 conditions are suitable for good machinability, It is widely used in mechanical parts, forgings, commercial vehicles, railway structural parts, shipbuilding, etc. the typical alloy 6082-o has good mechanical and physical properties, good weldability, good machinability, 20 ℃ (68 ℃) (% IACS) 51 tensile strength (25 ° C MPa) 150 yield strength (25 ° C MPa) 85 hardness 500kg force 10mm ball 40 elongation 1.6mm (1 / 16in) thickness 22% typical alloy 6082-T6 / t651 good mechanical and physical properties weldability good machinability good conductivity 20 ℃ (68 ℃) (% IACS) 42 tensile strength (25 ° CMPA) 315 yield strength (25 ° CMPA) 280 hardness 500kg force 10mm ball 94 elongation 1.6mm (1 / 16in) thickness 12%
About quality control
To keep the aluminum billet quality good ,each 25 ton will test 5 pcs to check the composition, as photo showed our lab will test 5 times for the aluminum billet.
In past 15 years, over 45 countries clients importing the billet from us and continued as our quality is reliable.
Aluminum alloy rods of various alloys can be produced by using aluminum ingots and blending other alloy components.
The specifications of aluminum billet are: 90m, 100mm, 120mm, 150mm, 178mm which used more .